Property | Test Method | Value or Rating |
Density: | ASTM D1667 | 300-400 kg/m³ |
Hardness: Shore 00 | ASTM D2240 | 40-55 |
Holding Power: | ASTM D3654/D3654M-06(2011) | >72h |
Initial Tack: | ASTM D3121-06 | 8.2mm |
180°Peel Strength: | ASTM D3330/D3330M-04(2010) | 0.82N/mm |
90° Peel Adhesion: | AAMA 810.1 | 855 N/mm |
Shear Strength: | ASTM D1002-2010 | 0.16N/mm² |
Compression Set: | AAMA 810.1 | 0.7% |
Compression Deflection: | AAMA 810.1 | 55KPa |
Tensile Strength: | AAMA 810.1 | 400KPa |
Elongation At Break: | ASTM D412 | 100-130% |
Force to Compress : | AAMA 810.1 | 70KPa |
Water Absorption | AAMA 810.1 | 1% |
Flammability | UL-94-2013 FMVSS 302 | HB Pass |
Dynamic Tensile Adhesion: | NTP-11 | 307-365KPa |
Dynamic Shear Adhesion: | NTP-5 | 200-255KPa |
Static Shear Adhesion: Hours 1 psi load* | NTP-57 | 1900+ |
Thermal Conductivity K factor: | ASTM C518 | 0.06w/m•°C |
Migratory Staining of Acrylic Enamel: 200 hours of ultraviolet at 140°F | ASTM D925 | No Staining |
Service Temperature | -- | -40°C to 80°C |
Application Temperature: | -- | 15°C to 50°C |
Resistance(Ba Rebound) | ASTM D3574-H | 21% |